|Key Words:||Bentonite Mineral Powder||Products:||Paint Raw Materials|
|Raw Material:||Bentonite||HS Code:||38249999|
|Other Name:||Organoclay Rheological Additive||Appearance:||White Powder|
|Material:||Bentonite,95% Montmorillonite||Grade:||Paint Industry|
sodium based bentonite powder,
bentonite grease alternative
Organoclay Bentonite CP-720B
Organoclay Bentonite CP-720B is a kind of new organoclay rheological additive. Organoclay Viscosifiers is high purified and special modified. Ÿ Rheology organoclay is used in systems covering low polarity, medium and high polarity range solvent and resin system.
Composition Organic derivative of a montmorillonite clay
Appearance Fine powder, white
Moisture content (105℃,2hr) ≤3.5%
Loss on ignition (1000℃) 40%-44%
Bulk density 0.40~0.60g/cm3
Fineness (<74μm, %) ≥99.8%
Dispersion fineness (μm) ≤10
High purity, low silica content.
Easy dispersing, fine particle size. Easy to use, no need to pregel
High viscosity and high thixotropic.
Wide application range. It can be applied in almost all resins and solvents
Gel is very transparent and of light color.
Organoclay rheological additive CP-720B is used in the following applications:
Paints including top grades paint, decorative paint, industrial paint, traffic paint etc.
1. Pre-gel method
A. Polar activator is not necessary:
a. Main solvent xylene: 95~92%
b. Rheology organoclay CP-720B:5~8%
c. Dispersing 5-15min, gel is finished.
B. Polar activator is necessary:
a. In aromatic solvent, the recommend activator is methyl acohol/water (95%/5%)/ acolhol/water (95%/5%), the dosage is 33%-45% based on the weight of CP-720B.
b. In mineral oil (such as 200#), white oil, diesel oil, the recommend activator is methyl acohol/water (95%/5%)/acolhol/water(95%/5%), the dosage is 33%-60% based on the weight of CP-720B.
2. Procedure of adding gel:
A. Charge solvent and resin to mill
B. Slowly add the gel
C. Dispersing 5-10min
D. Wetting agent (if required)
E. Disperse completely to desired fineness
F. Dilute to desired viscosity
3. Add directly with powder
A. Charge solvent and resin
B. Add Organo bentonite CP-720B slowly
C. Disperse 10-15min
D .Add polar activator (if necessary)
E. Disperse 10-15min at high speed
F. Add wetting agent and other additive
G. Grind and next procedure
Solvent Borne Organoclay can be added directly in powder under high shear condition. The addition is recommended to be before grinding procedure to get the best effectiveness. Addition level is commonly 0.1%~2.0%. If add polar activator and make pre-gel, better efficiency can be achieved.
All safety information is provided in the Material Safety Data Sheets for Zhejiang Camp-Shinning New Material Co., Ltd.
Kraft paper bag with PE liner or multi-wall paper sacks or customized. 25kg/bag or 22.68kg/bag or customized
Solvent based Organoclay CP-720B has a shelf life of 2 years, and should be stored in ventilated cool and dry place.
The information on use is based on data which are believed reliable, but any recommendation or suggestion made is without guarantee or warranty, since the conditions of use are outside our control. Organoclay Bentonite are sold on the conditions that purchasers shall make their own tests to determine the suitability of such products for their purpose and that all risks are assumed by user. We disclaim any responsibility for damages resulting from careless or improper handling or use. Nothing herein is to be taken as permission, inducement or recommendation to practice any patented invention without a license.
|COMPOSITION||Organic derivative of a bentonite clay|
|Moisture content (105℃,2hr) %||≤3.50|
|FINENESS (<74μm, %)||≥98.0|
|Appearance||Fine powder, white|